Pengaruh Penambahan Serat Pohon Bambu Ampel (Bambusa Vulgaris) pada Komposit Hybrid untuk Material Bumper Kendaraan Bermotor

Authors

  • Gito Mulyo Inggit Bagus Satria Universitas Tidar
  • Sri Hastuti Universitas Tidar
  • Ikhwan Taufik Universitas Tidar

DOI:

https://doi.org/10.55606/jtmei.v3i4.4523

Keywords:

Composite hybrid, car bumpers, impact test, tensile test

Abstract

Technological developments continue to increase in line with the times, producing various innovations that provide benefits to society, especially in the material sector. The use of a mixture of natural and synthetic fibers in composites (hybrid) has produced a stronger material, which can function as an alternative material for car bumpers. This research was carried out with the aim of determining the values ​​of impact toughness, tensile strength, and failure patterns that occur in the fracture cross section of the specimen through macro photographs. In this research, a hybrid composite was formed by combining ampelous bamboo fiber, fiberglass, and polyester resin. Variations in volume fraction applied include: 5%:25%:70%, 10%:25%:65%, and 15%:25%:60%. The specimens were formed according to ASTM E23 standards for impact tests and ASTM D638 for tensile tests. The results of the impact and tensile tests showed that the lowest value of impact toughness was 0.0744 J/mm² and tensile stress was 120.29 MPa. Meanwhile, the highest value for impact toughness was 0.0986 J/mm² and the tensile stress value was 147.65 MPa. Macro photo analysis of the fracture cross section is categorized as splitting in multiple areas and the fracture cross section also shows debonding and fiber pull out after the fracture occurred.

Downloads

References

Abdullah, G., & Handiko, G. W. (2000). Aplikasi komposit GFRP untuk front end KRL-Nas dan KRLI. INKA, Madiun.

Chaowana, P., & Barbu, M. C. (2017). Bamboo: Potential material for biocomposites. In Lignocellulosic fibre and biomass-based composite materials (pp. 259–289). https://doi.org/10.1016/B978-0-08-100959-8.00013-5

Diharjo, K. (2006). Pengaruh perlakuan alkali terhadap sifat tarik bahan komposit serat rami-polyester. Jurnal Teknik Mesin, 8(1), 8–13. Universitas Kristen Petra Surabaya.

Hanifi, R., Dewangga, G., & Widianto, E. (2019). Analisis material komposit berbasis serat pelepah kelapa sawit dan matriks polypropylene sebagai bahan pembuatan bumper mobil. Gorontalo Journal of Infrastructure and Science Engineering, 2(2), 15–23.

Hariyanto, A. (2015). Peningkatan kekuatan tarik dan impak pada rekayasa dan manufaktur bahan komposit hybrid berpenguat serat E-glass dan serat kenaf bermatrik polyester untuk panel interior automotive. Fakultas Teknik Universitas Wahid Hasyim Semarang, 6(1), 1–6.

Lutfi, F. (2018). Pembuatan model papan selancar komposit serat bambu menggunakan metode vacuum bagging.

Nugraha, A. A., Diharjo, K., & Raharjo, W. W. (2020). Pengaruh kandungan serat dan perlakuan alkali terhadap sifat tarik, bending, dan impak bahan komposit serat aren-polyester. Jurnal Teknik Mesin Indonesia, 15(2), 34–38.

Pratama, Y. Y., Setyanto, R. H., & Priadythama, I. (2014). Pengaruh perlakuan alkali, fraksi volume serat, dan panjang serat terhadap kekuatan tarik komposit serat sabut kelapa-polyester.

Priyanto, K., Purwono, A. H., & Cristanto, D. A. (2019). Ketangguhan impak dan kekuatan tarik komposit fiberglass/clay filler bermatriks unsaturated polyester Bqtn-Ex 157. Teknika, 6(2), 45–53.

Riyanto, A., & Irfa'I, M. A. (2018). Pengaruh fraksi volume serat komposit hybrid berpenguat serat bambu acak dan serat E-glass anyam dengan resin polyester terhadap kekuatan bending. Jurnal Teknik Mesin, 06(02), 55–60.

Rochim, M. N., & Ningsih, T. H. (2021). Penggunaan serat jerami padi dalam pembuatan material komposit sebagai alternatif bahan bumper mobil. Jurnal Teknik Mesin, 9(3), 1–6.

Saidah, A., Sri Endah, S., & Yos, N. (2018). Pengaruh fraksi volume serat terhadap volume dan orientasi serat terhadap kekuatan tarik komposit berbahan serat rami epoxy sebagai bahan alternatif komponen otomotif. In Seminar Nasional Teknik Mesin (Vol. 3, pp. 191–197).

Wahyudi, F. A., & Yuono, L. D. (2017). Pengaruh komposisi serat terhadap kekuatan impak komposit yang diperkuat serat bambu. Turbo: Jurnal Program Studi Teknik Mesin, 4(2), 72–78.

Wirawan, W. A., Setyabudi, S. A., & Widodo, T. D. (2017, October). Pengaruh jenis matrik terhadap sifat tarik pada natural fiber komposit. In Seminar Nasional Teknologi Terapan (MESIN) (Vol. 3, No. 01, pp. 29–34).

Downloads

Published

2024-11-15

How to Cite

Gito Mulyo Inggit Bagus Satria, Sri Hastuti, & Ikhwan Taufik. (2024). Pengaruh Penambahan Serat Pohon Bambu Ampel (Bambusa Vulgaris) pada Komposit Hybrid untuk Material Bumper Kendaraan Bermotor . Jurnal Teknik Mesin, Industri, Elektro Dan Informatika, 3(4), 148–156. https://doi.org/10.55606/jtmei.v3i4.4523